1. During the initial electrolytic polishing process, the polishing solution may foam. Therefore, the distance between the surface of the polishing solution and the top of the polishing tank should not be less than 15cm. Shenghua Litong stainless steel electrolyte, which does not foam, can be used.
2. Before entering the polishing tank, stainless steel workpieces should have as much residual moisture removed from their surface as possible. Excessive moisture can cause severe pitting and partial corrosion on the polished surface, rendering the workpiece unusable.
3. During the electrolytic polishing process, the iron and chromium elements contained in the stainless steel workpiece, acting as the anode, are continuously converted into metal ions and dissolved into the polishing solution, rather than depositing on the cathode surface. As the polishing process progresses, the concentration of metal ions continuously increases. When a certain value is reached, these metal ions precipitate out of the polishing solution as phosphates and sulfates, settling at the bottom of the polishing tank. Therefore, the polishing solution must be filtered regularly to remove these solid precipitates. Shenghua Litong stainless steel electrolyte, manufactured using the latest technology, effectively addresses the issue of excessive precipitates.
4. During the polishing process, in addition to the continuous consumption of phosphoric acid and sulfuric acid, water is lost due to evaporation and electrolysis. Furthermore, the high-viscosity polishing solution is continuously lost due to workpiece inclusion, causing the polishing solution level to drop. Therefore, it is necessary to frequently replenish the polishing tank with fresh polishing solution and water.
5. The neutralized discharge complies with current environmental protection requirements.
6. This product is corrosive. Avoid contact with eyes, mouth, and skin. If contact occurs, immediately flush with water. For severe cases, seek medical attention for strong acid burns.
7. Store in a sealed, cool place. It is effective for a long time.